I. Magnetic, thermal and transport properties of YbCu$_{5-x}$Zn$_x$ alloys
Authors
I. Čurlik
F. Akbar
S. Gabani
M. Giovannini
J. G. Sereni
Abstract
Within the family of cubic YbCu$_4$X compounds ($X$ = Ni, Au and Zn), we have investigated the YbCu$_{5-x}$Zn$_x$ ($1\geq x \geq 0.7$) alloys by means of structural, magnetic, thermal and transport measurements. In the $τ1-$ YbCu$_{5-x}$Zn$_x$ (cubic AuBe$_5$ type, $0.7 \leq x \leq 1.5$) structural phase, Yb ion is in its Yb$^{3+}$ magnetic configuration. However, by increasing Zn content the unit cell grows faster than a reference computed as a Cu by Zn atoms substitution, which indicates a shift of Yb ions towards the larger Yb$^{2+}$ configuration. The magnetic behavior confirms such tendency with a clear decrease of the saturation magnetization and effective moment between $x=0.7$ and $x=1$. The specific heat at low temperature shows a logarithmic dependence characteristic for a non-fermi-liquid behavior. The characteristic energies of all studied parameters, including magneto resistivity, show notably low values as an indication that these alloys are close to a quantum critical point, which is approached from the non-magnetic side as the Zn content decreases.